>>892159>"prove it" is the same kind of bullshit as "constructive criticism" that morons like you run away to when they have no argument.If you think the burden of proof and constructive criticism are bullshit. If you really believe that, I pity you.
We're not comparing a 3mm thick stainless clip point to an 7mm kukri made from a leaf spring.
They're both
-4 inch clip points
-nearly the same thickness.
-same steel
-same heat treat
I'm saying that because the blades are similar in so many significant way that a claim that one out performs the other is extraordinary and requires proof.
I have a hard time believing that grinding in a faux distal taper to a blade will significantly increase its work performance. In fact, if the grinding leaves a rough surface it may actually reduce performance.
http://www.cartercrafts.com/carbon_myth.htm (Mirror Polished Blades - Too Pretty To Use)
Now look at the pic. There's good reason to believe the roughly finished Kansbol may actually be negatively effected by it's finish. Further reason to require proof from you back up your claim that the Kansbol out performs the Companion.